ANALISA KOMPARASI PEMBENTUKAN KERAK KUPRI KARBONAT (CuCO3) PADA PIPA BOILER DAN PIPA SIMULATOR

Adi, Noviyanto (2019) ANALISA KOMPARASI PEMBENTUKAN KERAK KUPRI KARBONAT (CuCO3) PADA PIPA BOILER DAN PIPA SIMULATOR. Sarjana / Sarjana Terapan (S1/D4) thesis, Universitas Muhammadiyah Semarang.

Text FULL TEXT WORD.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

ABSTRAK ANALISA KOMPARASI PEMBENTUKAN KERAK KUPRI KARBONAT (CuCO3) PADA PIPA BOILER DAN PIPA SIMULATOR Oleh : Adi Noviyanto C2A015002 Program Studi Teknik Mesin Fakultas Teknik Universitas Muhammadiyah Semarang e-mail : adinoviyanto88@gmail.com Kerak tembaga karbonat (CuCO3) yang mengendap pada dinding pipa diselidiki dalam penelitian ini. Kerak tembaga karbonat adalah kerak yang sering terbentuk pada pipa boiler. Dalam eksperimental, larutan pembentuk kerak disiapkan dengan mencampurkan larutan equimolar CuCl2 dan Na2CO3. Tujuan dari penelitian ini adalah untuk membandingkan hasil penelitian tentang pembentukan kerak CuCO3 pada pipa boiler kerak CuCO3 dan pada pipa simulasi dengan suhu 300-4000C. Kerak yang terbentuk kemudian dievaluasi menggunakan analisis karakteristik kerak dan SEM/EDX. Hasil penelitian menunjukkan bahwa kerak memiliki pelat seperti morfologi dan kerak fase kristal yang ditemukan sebagian besar malasite. Berdasarkan hasil ini, kerak CuCO3 di Boiler memiliki kondisi panas yang sangat tinggi dan waktu panas yang lama membuat kerak CuCO3 berwarna hitam. Warna dan tekstur kerak CuCO3 pada pipa menunjukkan warna yang lebih cerah. Kerak yang terbentuk kemudian dievaluasi menggunakan analisis SEM / EDX. Perbandingan analisis antara hasil analisis kerak CuCO3 pada pipa boiler dan pipa simulator menunjukkan hasil yang berbeda. Hasil analisis SEM menunjukkan bahwa kristal yang dilakukan melalui eksperimen diambil dari boiler dan pipa. Perbedaan morfologi dan komposisi antara sampel kedua adalah karena boiler lebih panas daripada di pipa sehingga morfologi kristal CuCO3 dalam boiler lebih rapat dibandingkan di pipa. Kata kunci : Cupri Carbonate, Comparasi, Pipa Boiler, Pipa Simulator, SEM-EDX, Morfologi Kerak ABSTRACT COMPARATION ANALYSIS OF THE FORMATION OF SCALE CUPRI CARBONATE (CuCO3) IN BOILER PIPES AND SIMULATOR PIPES by: Adi Noviyanto C2A15002 Mechanical Engineering Study Program, Faculty of Engineering Universitas Muhammadiyah Semarang e-mail : adinoviyanto88@gmail.com Abstract The cupri carbonate scale (CuCO3) deposited on the pipe wall was investigated in this study. Carbonate copper scale is a scale that often forms on boiler pipes. In the experimental work, the scale-forming solution was prepared by mixing equimolar solutions CuCl2 and Na2CO3. The purpose of this study was to compare the results of research on CuCO3 scale formation on boiler pipes and CuCO3 scale in simulated pipes with temperatures of 300-4000C. The scale formed is then evaluated using scale characteristic analysis and SEM / EDX. The results showed that the scale had plates such as morphology and scale crystalline phase found mostly malachite. Based on these results, the CuCO3 scale in the Boiler has very high heat conditions and long heat times making the color of the CuCO3 scale formed black. The color and texture of CuCO3 scale on the pipe shows a brighter color. The scale formed is then evaluated using SEM / EDX analysis. Comparison of the analysis between the results of CuCO3 scale analysis on boiler pipes and simulator pipes shows different results. The results of SEM analysis showed that crystals carried out through experiments were taken from boilers and pipes. The morphological difference between the second sample is due to the boiler being hotter than in the pipe so the crystalline morphology of CuCO3 in the boiler is more than the meeting than in the pipe. Keywords: Cupri Carbonate, Comparation, boiler pipe, simulator pipe, SEM-EDX, scale morphology

Actions (login required)

View Item