EKSPERIMEN PEMBENTUKAN KERAK MAGNESIUM (Mg) PADA PIPA BERALIRAN LAMINER DENGAN PARAMETER LAJU ALIR 30 ML/MINUTES DAN PENAMBAHAN ADITIF ION CU2+ 20 PPM

KURNIAWAN, ACHMAD DWI, C2A014010 (2018) EKSPERIMEN PEMBENTUKAN KERAK MAGNESIUM (Mg) PADA PIPA BERALIRAN LAMINER DENGAN PARAMETER LAJU ALIR 30 ML/MINUTES DAN PENAMBAHAN ADITIF ION CU2+ 20 PPM. Sarjana / Sarjana Terapan (S1/D4) thesis, ["eprint_fieldopt_institution_Universitas Muhammadiyah Semarang" not defined].

[img]
Preview
Text
ABSTRAK.pdf

Download (58kB) | Preview
[img]
Preview
Text
BAB 1.pdf

Download (268kB) | Preview
[img]
Preview
Text
BAB 2.pdf

Download (1MB) | Preview
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (982kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Repository staff only

Download (373kB) | Request a copy
[img]
Preview
Text
BAB 5.pdf

Download (138kB) | Preview
[img]
Preview
Text
DAFTAR PUSTAKA.pdf

Download (173kB) | Preview

Abstract

EKSPERIMEN PEMBENTUKAN KERAK MAGNESIUM (Mg) PADA PIPA BERALIRAN LAMINER DENGAN PARAMETER LAJU ALIR 30 ML/MINUTES DAN PENAMBAHAN ADITIF ION CU2+ 20 PPM Oleh : Achmad Dwi Kurniawan C2A014010 Program Studi Teknik Mesin Fakultas Teknik Universitas Muhammadiyah Semarang Abstrak Industri yang menggunakan air dalam sistem kerjanya dipastikan bahwa selalu memiliki permasalahan dalam pengerakan.Hal ini disebabkan karena kerak dapat menutupi atau menyumbat air yang mengalir dalam pipa dan sekaligus menghambat proses perpindahan panas.Tujuan dilakukan penelitian ini untuk mengembangkan alat Simulator pembentuk kerak, memahami mekanisme pengendalian kerak MgCO3 dengan menggunakan penambahan aditif ion cu2+ 20 ppm di dalam pipa dan mengkaji hasil morfologi kerak. Hasil yang didapatkan selama pengujian dengan mereaksikan MgCl2 dan Na2CO3 menggunakan larutan Mg2+ berkonsentrasi 3000 ppm dengan pengukuran waktu induksi. Hasil penelitian ini didapatkan waktu induksi untuk tanpa penambahan adalah 24 menit dengan nilai konduktivitas 8522 µS/cm sedangkan pada penambahan aditif ion cu2+ 20 ppm nilai konduktivitas 8510 µS/cm pada lama waktu 40 menit. Dari hasil SEM menunjukan bentuk morfologi kerak MgCO3 yang semula berbentuk kubus menjadi betuk yang tidak beraturan dan berukuran lebih kecil. Kata Kunci : Kerak MgCO3, ION CU2+, Waktu Induksi, morfologi kerak. AN EXPERIMENT OF MAGNESIUM CRUST FORMATION (Mg) ON LAMINARY PIPE WITH PARAMETERS OF FLOW RATE 30 ML/MINUTES AND ADICTIVE ADDITION ION CU2+ 20 PPM By: Achmad Dwi Kurniawan C2A014010 Mechanical Engineering Department Faculty of Engineering University of Muhammadiyah Semarang Abstract Industry which is applied water in work system confirmed that always has the problem in the movement. It is caused by crust can block or clog the water which is flowing in the pipe and also clogging heat transfer process. This study purposes to developing crust forming simulator tool, identifying crust control mechanism MgCO3 by applying addictive ion addition cu2+ 20 ppm in the pipe and reviewing result of crust morphology. Result of this study during testing by reacting MgCl2 and Na2CO3 applied solvent Mg2+ concerned on 3000 ppm with induction time measurement. Result of this study found induction time without addition was 24 minutes with conductivity score 8522 µS/cm while on addictive ion addition cu2+ 20 ppm conductivity score was 8510 µS/cm during 40 minutes. Based on SEM results showed shape of crust morphology MgCO3 that first cube-shaped became irregular-shaped and smaller. Keywords: Crust MgCO3+, ION CU2+, Induction Time, Crust Morphology.

Item Type: Thesis (Sarjana / Sarjana Terapan (S1/D4) )
Contributors Thesis: 1. Drs. H. Samsudi Raharjo ST., MM., MT 2. Rubijanto Juni P ST., MT
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Engineering > S1 Mechanical Engineering
Depositing User: perpus unimus
Date Deposited: 25 Mar 2019 04:27
Last Modified: 25 Mar 2019 04:27
URI: http://repository.unimus.ac.id/id/eprint/3123

Actions (login required)

View Item View Item